Renault Wear Test Standard: KY-Car Woven Protective Sleeves, C66-1680
2024-06-24
TEST REPORT
No. : KY 20221115003-En
Date : February 20, 2024
Page : 1 of 6
CUSTOMER NAME: Dongguan Keyu New Materials Technology Co.,Ltd
ADDRESS: Building B, West Gate, Haoyu Industrial, Miao Bian Wan Village,
Shi Pai Town, Dongguan City, GD523343, People's Republic of China
The following sample information(s) was/were provided and identified on behalf of the client as:
Report No: KY 20221115003-En.
Sample Name: KY-Car Woven Protective Sleeves
Part Number: KY1130
Sample material: PET+PA66
Sample number: KY 211215001
Date received: December 15, 2021
Test start date: January 5, 2022
Testing end date: March 3, 2022
Test results: More information can be found on the following pages.
Posted by: Mr. Yang. Checked by: MR. Liao
Approved by: Mr. Wei. Approval date: February 20, 2024
TEST REPORT
No. : KY 20221115003-En
Date : February 20, 2024
Page: 2 of 6
Report Declaration:
This report is void if modified without the signature of the approver or without a special seal of the laboratory report;
The samples tested in this report are provided and verified by the applicant and the testing center is not responsible for verifying their authenticity;The test results in this report refer to incoming samples only;
Partial reproduction of this report is not permitted without the written consent of this testing center.
Test result:
| number | Test item | Link. Standard | Evaluation |
| 1 | Abrasion resistance | STL S21 5101 Rev.A-2010
& D44 1959 Rev. A-2010 Client requirements |
Past |
Note: Pass: meets requirements
Failed: Does not meet requirements.
N/A: Does not apply to judges.
TEST REPORT
No.: Kentucky 20221115003-January
Date: February 20
Page : 3 of 6
Test object: abrasion resistance
Sample Description: Black expandable shell. Laboratory environment conditions: 25°C, 54% relative humidity.
Test method: STL S21 5101 Rev.A-2010 and D44 1959 Rev.A-2010 &Customer requirements
Customer Requirements: Meets D44 1959-2010 Class D, Aging Conditions: 150℃ and 1000H Test Conditions:
Wear tool: Grade D-Plastic Edge PA66-GF30 Offset: ±5mm
Frequency: 10Hz ± 1Hz. Test temperature: 120 °C. Mandrel diameter: Φ13mm. Load: 200 g.
Test procedure: 144,000 times (4 hours) before aging, 36,000 times (1 hour) after aging at
150℃ and 1000 hours
Friction type: